2017-01-01
Spinelli, J.E., Hearn, W., Bogno, A.-A., Henein, H.
Understanding the influence of rapid solidification conditions on the formed microstructure is important to determine how process conditions affect the final mechanical properties. In this work the rapid solidification of hypoeutectic and hypereutectic Al-xSi (x=10wt. %, 18wt %) alloys was...
-
2016-01-01
Bogno, A.-A., Riveros, C., Henein, H., Li, D.
This paper investigates amorphous phase formation and rapid solidification characteristics of a CoCr alloy. High cooling rate and high undercooling-induced rapid solidification of the alloy was achieved by impulse atomization in helium atmosphere. Two atomization experiments were carried out to...
-
Characterization of a {(Fe60Co40)75B20Si5}96Nb4 Impulse Atomized Glassy Powder by Neutron Diffraction and Differential Scanning Calorimetry
Download2015-01-01
Bogno, A.-A., Dahlborg, U., Calvo-Dahlborg, M., Riveros, C., Ciftci, N., Henein, H., Sediako, D.
This paper investigates FeCo-based alloy glass formability by high undercooling and high cooling rate solidification technique and the hardness evaluation of the generated samples. For this investigation, Impulse Atomization was used to generate {(Fe60Co40)75B20Si5}96Nb4 powders of different...
-
2016-01-01
Bedel, M., Reinhart, G., Bogno, A.-A., Gandin, Ch.-A., Jacomet, S., Boller, E., Nguyen-Thi, H., Henein, H.
The Impulse Atomization process developed at the University of Alberta (Canada) enables metallic powders to be solidified with well controlled process parameters. The inner microstructure of several droplets of Al-4.5wt.%Cu alloy produced by this technique has been investigated by using both...
-
Design and processing conditions of hypoeutectic Al-Cu-Sc alloys for maximum benefit of scandium
Download2017-01-01
Bogno, A.-A., Henein, H., Gallerneault, M.
Addition of Sc to Al-Cu is reported to be responsible for a high precipitation hardening upon heat treatment and serves as a good grain refiner. However, Scandium is presently very expensive, therefore, getting maximum benefit from a minimum addition would be economically of value. This work...
-
EFFECTS OF SCANDIUM ON HYPO-EUTECTIC ALUMINUM COPPER MICROSTRUCTURES UNDER LOW SOLIDIFICATION RATE CONDITIONS
Download2017-11-01
Bogno, A.-A., Valloton, J., Henein, H., Ivey, D.G., Locock, A.J., Gallerneault, M.
This work addresses the microstructures and mechanical properties of Al-4.5 wt% Cu alloys containing 0.1, 0.2 and 0.4 wt% Sc that were solidified under low cooling rate conditions (< 1ºC/s) and then heat treated. The samples were solidified in a differential scanning calorimeter before being heat...
-
2019-01-01
Bogno, A.-A., Henein, H., Ivey, D.G., Valloton, J., Reinhart, G., Sediako, D., Gallerneault, M.
This paper reports on the characterization of rapidly solidified Al-4.5 wt% Cu-xSc (x= 0.1, 0.2 or 0.4 wt %). The effect of micro-additions of Sc (up to 0.4 wt %) was examined through microstructural analysis of rapidly solidified, as well as aged samples, by means of electron microscopy, x-ray...
-
Fabrication of aluminum/stainless steel bimetallic composites through a combination of additive manufacturing and vacuum-assisted melt infiltration casting
Download2021-01-01
Ghasri-Khouzani, M., Li, X., Bogno, A.-A., Chen, Z., Liu, J., Henein, H., Qureshi, A.J.
This paper provides a hybrid method for net shape, lattice based, complex bimetallic composites using a combination of laser powder bed additive manufacturing and vacuum-assisted melt infiltration casting process. 316L stainless steel lattice structures were built using a selective laser melting...
-
Influence of Annealing Treatment on Si Morphology and Strength of Rapid Solidified Al-12 wt.% Si Powders
Download2018-01-01
Gomes, L.E., Spinelli, J.E., Bogno, A.-A., Gallerneault, M., Henein, H.
An experimental study is reported on heat treating rapid solidified Al-12 wt.% Si alloy with 355-425 m powder size. Fast heat treatments at 813K revealed morphological shifts of eutectic Si from the as-atomized condition to those after annealing. The Si network of the as-atomized samples showed...
-
Investigation of Compressive and Tensile Behavior of Stainless Steel/Dissolvable Aluminum Bimetallic Composites by Finite Element Modelling and Digital Image Correlation
Download2021-01-01
Li, X., Ghasri-Khouzani, M., Bogno, A.-A., Liu, J., Henein, H., Chen, Z., Qureshi, A.J.
This study reports fabrication, mechanical characterization, and finite element modeling of a novel lattice structure based bimetallic composite comprised of 316L stainless steel and a func-tional dissolvable aluminum alloy. A net-shaped 316L stainless steel lattice structure composed of diamond...