Valloton, J., Bogno, A.-A., Rappaz, M., Henein, H.
Rapid solidification of Al-Cu droplets of eutectic composition was carried out using Impulse Atomization (a type of drop tube). Two distinct morphologies were observed: an irregular undulated eutectic assumed to form during recalescence, followed by a regular lamellar eutectic. The volume...
-
Quantification of Dendritic and Eutectic Nucleation Undercooling in Rapidly Solidified Hypo-Eutectic Al-Cu Droplets
Download2016-01-01
Bogno, A.-A., Delshad Khatibi, P., Henein, H., Gandin, Ch.-A.
This paper reports on the quantification of primary dendritic and eutectic nucleation undercoolings during rapid solidification of impulse atomized hypo-eutectic Al-Cu droplets. The procedure consists in determining the eutectic fraction of each investigated droplet from the fraction of...
-
2018-01-01
Bogno, A.-A., Valloton, J., Jimenez, D.D., Rappaz, M., Henein, H.
Near eutectic Al-Cu droplets were rapidly solidified by Impulse Atomization. A wide range of microstructural scales was obtained at different cooling rates and undercoolings. The micrographs of the investigated samples revealed two distinct zones of different structural morphologies: An undulated...
-
2019-01-01
Valloton, J., Bogno, A.-A., Henein, H., Herlach, D.M., Sediako, D.
This paper reports on the undercooling and growth morphology of Al-4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc with a focus on the effect of Sc addition. It is found that the addition of Sc reduces the undercoolings of both primary phase and eutectic. In addition, the morphology of the Al-4.5wt%Cu-0.4wt%Sc...
-
2018-01-01
Valloton, J., Bogno, A.-A., Henein, H., Herlach, D.M., Sediako, D.
This paper reports on the undercooling and growth morphology of Al-4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc with a focus on the effect of Sc addition. It is found that the addition of Sc reduces the undercoolings of both primary phase and eutectic. In addition, the morphology of the Al-4.5wt%Cu-0.4wt%Sc...
-
The Microstructure, Morphology and Mechanical Properties of Rapidly Solidified Al-10wt%Si Alloy
DownloadSpring 2018
Hypoeutectic Al-Si alloys are widely used in both the automotive and aerospace industries, due to their strong corrosion resistance, good castability and relatively high strength-to-weight ratio. Despite this wide use, these alloys have a major limitation related to the Si phase that forms...