Spring 2011
Stainless steel is one of the most commonly used materials in most industries. Excellent corrosion resistance of stainless steel is due to the formation of an oxide film on the surface (passive film), which protects the material from continuous corrosion attacks. When subjected to an attack...
-
Effects of Oxide Additions on the Corrosion Behaviour of Cr2O3 Based Ceramics in High Temperature Supercritical Water Environment
DownloadFall 2012
This investigation is aimed at developing ceramic materials applied in supercritical water, which is being considered as coolant for one of the next generation nuclear reactors. Cr2O3, a primary protective film on stainless steels, was found to be unstable in SCW due to the formation of soluble...
-
Spring 2013
As the Supercritical Water-cooled Reactor (SCWR) shows a promising future, the corrosion behavior of candidate materials has attracted great interest. In this study, experimental investigation was conducted to evaluate the corrosion behavior of the ferritic-martensitic steels designed for the use...
-
Growth behavior of surface cracks in pipeline steels exposed to near-neutral pH environments
DownloadFall 2013
This study is part of a larger study designed to help a consortium of pipeline operators replace current (very expensive) approaches to managing stress corrosion cracking (SCC) concerns in near-neutral pH (NNPH) environments with mathematical models that predict SCC growth rates. This could...
-
Fall 2015
The present research has been done with the intent of evaluating the corrosion resistance and cracking susceptibility of some commercial candidate alloys that can be potentially used in Gen-IV supercritical water reactor (SCWR). The mechanism of the crack initiation in austenitic alloys exposed...
-
Fall 2015
Mechanical, tribological and corrosion properties of metallic materials are of significance to their industrial applications and have been studied for long time. Efforts are continuously made to correlate these properties to more fundamental parameters in order to effectively improve the...
-
Investigation of Corrosion and Crack Morphology Behavior under Disbonded Coatings on Pipelines
DownloadFall 2015
Coating disbondment on pipelines is a common phenomenon that leads to exposure of the pipeline metal to the surrounding soil and ground water solutions. The exposure of pipelines to those corrosive environments is associated with development of corrosion and Stress Corrosion Cracking (SCC) on the...
-
Spring 2015
This thesis presents a thorough examination of the corrosion and fouling behaviour of crude oil at refining conditions on industrially applicable heat transfer surfaces. The depletion of light sweet crude oil reserves means that the processing of ever heavier and more sour crude oils is...
-
The Role of Sulfur Species in Establishing the Corrosion Reactions in Refinery Metallurgies
DownloadSpring 2016
This thesis is focused on the studying the role that model sulfur-containing molecules have in corrosion reactions on relevant metallurgies. This was done by using a design of experiments where a number of sulfur-based compounds were reacted with various metallurgies. The 8 model sulfur compounds...
-
Fall 2016
Slurry pipelines are widely utilized in most mining operations to transport the raw materials and the tailings. These pipelines typically suffer from high wear rates. For example, in Canada’s oil sands industry, pipeline wear rates of 1 cm/yr are considered representative. To generate and measure...