Characterization of a {(Fe60Co40)75B20Si5}96Nb4 Impulse Atomized Glassy Powder by Neutron Diffraction and Differential Scanning Calorimetry
Download2015-01-01
Bogno, A.-A., Dahlborg, U., Calvo-Dahlborg, M., Riveros, C., Ciftci, N., Henein, H., Sediako, D.
This paper investigates FeCo-based alloy glass formability by high undercooling and high cooling rate solidification technique and the hardness evaluation of the generated samples. For this investigation, Impulse Atomization was used to generate {(Fe60Co40)75B20Si5}96Nb4 powders of different...
-
2016-01-01
Bogno, A.-A., Riveros, C., Henein, H., Li, D.
This paper investigates amorphous phase formation and rapid solidification characteristics of a CoCr alloy. High cooling rate and high undercooling-induced rapid solidification of the alloy was achieved by impulse atomization in helium atmosphere. Two atomization experiments were carried out to...
-
2016-01-01
Bedel, M., Reinhart, G., Bogno, A.-A., Gandin, Ch.-A., Jacomet, S., Boller, E., Nguyen-Thi, H., Henein, H.
The Impulse Atomization process developed at the University of Alberta (Canada) enables metallic powders to be solidified with well controlled process parameters. The inner microstructure of several droplets of Al-4.5wt.%Cu alloy produced by this technique has been investigated by using both...
-
Quantification of Dendritic and Eutectic Nucleation Undercooling in Rapidly Solidified Hypo-Eutectic Al-Cu Droplets
Download2016-01-01
Bogno, A.-A., Delshad Khatibi, P., Henein, H., Gandin, Ch.-A.
This paper reports on the quantification of primary dendritic and eutectic nucleation undercoolings during rapid solidification of impulse atomized hypo-eutectic Al-Cu droplets. The procedure consists in determining the eutectic fraction of each investigated droplet from the fraction of...
-
Design and processing conditions of hypoeutectic Al-Cu-Sc alloys for maximum benefit of scandium
Download2017-01-01
Bogno, A.-A., Henein, H., Gallerneault, M.
Addition of Sc to Al-Cu is reported to be responsible for a high precipitation hardening upon heat treatment and serves as a good grain refiner. However, Scandium is presently very expensive, therefore, getting maximum benefit from a minimum addition would be economically of value. This work...
-
2018-01-01
Valloton, J., Bogno, A.-A., Henein, H., Herlach, D.M., Sediako, D.
This paper reports on the undercooling and growth morphology of Al-4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc with a focus on the effect of Sc addition. It is found that the addition of Sc reduces the undercoolings of both primary phase and eutectic. In addition, the morphology of the Al-4.5wt%Cu-0.4wt%Sc...
-
2018-01-01
Bogno, A.-A., Valloton, J., Jimenez, D.D., Rappaz, M., Henein, H.
Near eutectic Al-Cu droplets were rapidly solidified by Impulse Atomization. A wide range of microstructural scales was obtained at different cooling rates and undercoolings. The micrographs of the investigated samples revealed two distinct zones of different structural morphologies: An undulated...
-
2019-01-01
Bogno, A.-A., Henein, H., Ivey, D.G., Valloton, J., Reinhart, G., Sediako, D., Gallerneault, M.
This paper reports on the characterization of rapidly solidified Al-4.5 wt% Cu-xSc (x= 0.1, 0.2 or 0.4 wt %). The effect of micro-additions of Sc (up to 0.4 wt %) was examined through microstructural analysis of rapidly solidified, as well as aged samples, by means of electron microscopy, x-ray...
-
2019-01-01
Valloton, J., Bogno, A.-A., Henein, H., Herlach, D.M., Sediako, D.
This paper reports on the undercooling and growth morphology of Al-4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc with a focus on the effect of Sc addition. It is found that the addition of Sc reduces the undercoolings of both primary phase and eutectic. In addition, the morphology of the Al-4.5wt%Cu-0.4wt%Sc...
-
2021-01-01
Valloton, J., Bogno, A.-A., Rappaz, M., Henein, H.
Rapid solidification of Al-Cu droplets of eutectic composition was carried out using Impulse Atomization (a type of drop tube). Two distinct morphologies were observed: an irregular undulated eutectic assumed to form during recalescence, followed by a regular lamellar eutectic. The volume...