Growth and Characterization of Metastable Hexagonal Nickel Thin Films via Plasma-Enhanced Atomic Layer Deposition

• Author(s) / Creator(s)

  • Motamedi, Pouyan
  • Bosnick, ken
  • Cui, Kai
  • Cadien, Ken
  • Hogan, James D.

• There is a great interest in various branches of the advanced materials industry for the development of novel methods (and improvements to existing ones) for the deposition of conformal ultrathin metallic films. In most of these applications, like enhanced solar absorbers and microelectronics, achieving the capacity to deposit a conformal thin film on a three-dimensional structure is an important condition. Plasma-enhanced atomic layer deposition (ALD) is known for its potential for growth of conformal thin films with a precise control over the thickness and its capability for deposition at relatively low temperatures (below 500 °C). This study evaluates the potential of plasma-enhanced ALD for growth of conformal nickel thin films, using bis(ethylcyclopentadienyl)nickel and nitrogen/hydrogen plasma as precursors. A comprehensive analysis of the structure, composition, and physical properties of the films was performed. The results indicate that conformal nickel films with low levels of impurity were successfully deposited on sapphire. The films had a roughness of Ra = 1.5 nm and were seen to be under strain. The deposited nickel had a hexagonal crystal structure, with a random in-plane orientation of the grains, while the grains had their c-axes oriented along the normal to the interface. These results pave the way for conformal low-temperature deposition of high-quality nickel thin films on three-dimensional structures.

• Date created

  2017-07-01

• Subjects / Keywords

  • Atomic layer deposition
  • Deposition
  • Nickel
  • Thickness
  • Thin films

• Type of Item

  Article (Draft / Submitted)

• DOI

  https://doi.org/10.7939/r3-2zv2-4s33

• License

  This document is the Accepted Manuscript version of a Published Work that appeared in final form in ACS Applied Materials & Interfaces, copyright © 2017 American Chemical Society after peer review and technical editing by the publisher. To access the final edited and published work see http://dx.doi.org/10.1021/acsami.7b05571