Skip to Search Results- 3Boron carbide
- 3Brittle failure
- 3Kolsky bar technique
- 1Confined compression
- 1Microstructural characterizations
- 1Nanoindentation
-
2016-01-01
Farbaniec, Lukasz, Hogan, James D., McCauley, James W., Ramesh, Kaliat T.
Effects of microstructure and material properties on the mechanical behavior of hot-pressed boron carbide are presented. The microstructure and intrinsic microstructural inhomogeneities have been characterized using scanning electron microscopy characterization techniques (SEM/EDS/EBSD). In-situ...
-
2017-01-01
Farbaniec, L., Hogan, James D., Xie, K.Y., Shaeffer, M., Hemker, K.J., Ramesh, K.T.
The dynamic response of hot-pressed boron carbide was studied under uniaxial and confined loading conditions using a modified compression Kolsky bar setup at strain rates of 102 – 103 s–1. The progression of damage in the prismatic specimens was captured using a high-speed camera. This...
-
Micromechanisms Associated with the Dynamic Compressive Failure of Hot-Pressed Boron Carbide
Download2015
Ramesh, K.T., Farbaniec, Lukasz, Hogan, James
Brittle failure in boron carbide has been studied in dynamic uniaxial compression using a Kolsky bar technique. A detailed study of fragments was performed using SEM-EDS, to identify the mechanisms responsible for failure. Microstructural characterization and fracture surface observations...