Assessment of Oxide Descaler Functionality in a Steel Hot Rolling Mill Using Infrared Video Imaging
Download2018-01-01
Wiskel, J.B., Linchieh, A., Henein, H.
A series of infrared temperature videos were taken of the upper surface of hot rolled microalloyed steel skelp immediately following laminar cooling. In addition to validation of the skelp temperature and skelp cooling patterns, local temperature minimums were observed in the infrared images....
-
CHARACTERIZATION OF X80 AND X100 MICROALLOYED PIPELINE STEEL USING QUANTITATIVE X-RAY DIFFRACTION
Download2018-01-01
Wiskel, J.B., Li, X., Ivey, D.G., Henein, H.
Quantitative X-ray diffraction characterization of four (4) X80 and three (3) X100 microalloyed steels was undertaken. The effect of through thickness position, processing parameters and composition on the measured crystallite size, microstrain and J index (relative magnitude of crystallographic...
-
Effect of cold wire addition in tandem submerged arc welding on weld geometry and micro-hardness of heavy gauge X70 steel
Download2022-01-01
Ren, T., Mohammadijoo, M., Wiskel, J.B., Lazor, R., Willett, E., Ivey, D.G., Henein, H.
The pipeline industry has undertaken an essential upgrade of well established X70 pipeline steel in heavy gauge pipes to fill the demand of increased operating pressures. A developed welding process, cold wire tandem submerged arc welding (CWTSAW), with improved deposition rate and travel speed...
-
2018-01-01
Kennedy, J.R., Wiskel, J.B., Ivey, D.G., Henein, H.
The potential exists to use ultrasonic shear velocity for real time microstructure assessment of the quenching step in the teat treatment of L80 steel pipe. L80 steel samples were austenitized and subsequently cooled in different quench mediums (water, oil, heated oil, air and furnace) to produce...
-
2016-09-01
Wiskel, J.B., Ma, J., Valloton, J., Ivey, D.G., Henein, H.
Strain aging of microalloyed steel pipe can occur at the relatively low temperatures associated with the pipe coating process and/or during long term storage. A Box-Behnken statistical design is used to determine the significant strain aging variables that affect the longitudinal yield strength...
-
The Effect of Skelp Thickness on Precipitate Size and Morphology for X70 Microalloyed Steel Using Rietveld Refinement (Quantitative X-ray Diffraction)
Download2018-01-01
Chatelier, C., Wiskel, J.B., Ivey, D.G., Henein, H.
Precipitates in thin-walled (11 mm) and thick-walled X70 (17 mm) microalloyed X70 pipe steel are characterized using Rietveld refinement (a.k.a. quantitative X-ray diffraction (QXRD)), inductively coupled plasma mass spectrometry (ICP), and energy-dispersive X-ray spectroscopy (EDX) analyses....
-
Time Dependence of Hydrogen Induced Cracking of X70 Pipeline Steel under Severe and Mild Sour Service Conditions using Ultrasonic Analysis
Download2020-01-01
Gawor, S., Wiskel, J.B., Ivey, D.G., Liu, J., Henein, H.
A standard NACE hydrogen induced crack test was used to evaluate the resistance of two compositions of X70 steel (X70-X (Ca/S ratio of 2.5) and X70-B (Ca/S ratio of <0.5)) under severe (pH = 2.7 and 100% H2S) and mild (pH = 5.5 and 100% H2S) sour service conditions. An ultrasonic technique was...
-
Transverse Strain Aging Behaviour of Uncoated Thick Walled X70 UOE Microalloyed Steel Pipes
Download2018-01-01
Wiskel, J.B., Ma, J., Ivey, D.G., Henein, H.
Transverse tensile samples were extracted from the centreline position of three different compositions of uncoated thick walled microalloyed X70 UOE pipe at a location 180° from the weld. Aging heat treatments of 5, 15, and 25 minutes and temperatures of 175, 215, and 255°C were applied. Tensile...