Farbaniec, L., Hogan, James D., Xie, K.Y., Shaeffer, M., Hemker, K.J., Ramesh, K.T.
The dynamic response of hot-pressed boron carbide was studied under uniaxial and confined loading conditions using a modified compression Kolsky bar setup at strain rates of 102 – 103 s–1. The progression of damage in the prismatic specimens was captured using a high-speed camera. This...
-
2020-07-01
Lo, Calvin, Sano, Tomoko, Hogan, James D.
We investigated the uniaxial compressive behavior of damaged and intact alumina using quantitative X-ray computed tomography (XCT) analysis coupled with digital image correlation (DIC) for mechanical characterization. Internal three-dimensional crack characteristics such as crack surface area and...
-
2021-03-01
Koch, Brendan M.L., Lo, Calvin, Li, Haoyang, Sano, Tomoko, Ligda, Jonathan, Hogan, James D.
This paper explores the compressive responses of alumina ceramics subjected to various levels of pre-damage via internal cracking. Pre-damage is achieved by subjecting the samples to thermal shock. Mechanical loading is performed using a load frame for quasi-static strain rates and a Kolsky bar...
-
2017-04-01
Hogan, James D., Farbaniec, Lukasz, Mallick, Debjoy, Domnich, Vladislav, Kuwelkar, Kanak, Sano, Tomoko, McCauley, James W., Ramesh, Kaliat T.
In this paper, the impact-induced fragmentation of a commercially available hot-pressed boron carbide is explored. Fragmentation has been noted previously by many authors to be important in the impact performance of advanced ceramics, and so this paper seeks to provide some of the first...
-
Microstructural and mechanical characterization of variability in porous advanced ceramics using X-ray computed tomography and digital image correlation.
Download2019-01-01
Lo, Calvin, Sano, Tomoko, Hogan, James D.
This paper explores microstructural and mechanical variability in porous ceramics, combining advanced X-ray computed tomography (XCT) and digital image correlation (DIC) techniques to characterize an alumina material. The results show low variability in microstructure, with median pore size...
-
Quasi-static confined uniaxial compaction of granular alumina and boron carbide observing the particle size effects
Download2019-10-25
Nicewicz, Piotr, Peciar, Peter, Macho, Oliver, Sano, Tomoko, Hogan, James D.
The quasi-static confined uniaxial compaction of granular alumina and boron carbide was studied, and the effect of triaxial stress on the materials as a function of increasing particle size was observed. The average particle sizes studied for granular alumina were 170 ± 63, 230 ± 55, 330 ± 67,...
-
The effects of defects on the uniaxial compressive strength and failure of an advanced ceramic
Download2016
Ramesh, K., Farbaniec, Lukasz, Hogan, James D., Sano, Tomoko, Shaeffer, Matthew
This study investigates the effects of the processing-induced defect population on the dynamic compressive strength and failure of a hot-pressed boron carbide. Quantitative microscopic analysis was used to determine the distributions of three types of processing-induced inhomogeneities: aluminum...