Micromechanisms Associated with the Dynamic Compressive Failure of Hot-Pressed Boron Carbide
Download2015
Ramesh, K.T., Farbaniec, Lukasz, Hogan, James
Brittle failure in boron carbide has been studied in dynamic uniaxial compression using a Kolsky bar technique. A detailed study of fragments was performed using SEM-EDS, to identify the mechanisms responsible for failure. Microstructural characterization and fracture surface observations...
-
2016-01-01
Farbaniec, Lukasz, Hogan, James D., McCauley, James W., Ramesh, Kaliat T.
Effects of microstructure and material properties on the mechanical behavior of hot-pressed boron carbide are presented. The microstructure and intrinsic microstructural inhomogeneities have been characterized using scanning electron microscopy characterization techniques (SEM/EDS/EBSD). In-situ...
-
2016
Farbaniec, Lukasz, Daphalapurkar, Nitin, Ramesh, K.T., Hogan, James
Dynamic brittle fragmentation is typically described using analytical and computational approaches for tensile stress-states. However, most fragmentation applications (e.g., impact, blast) involve very large initial compressive stresses and deformations. In this study, the compressive...
-
The effects of defects on the uniaxial compressive strength and failure of an advanced ceramic
Download2016
Ramesh, K., Farbaniec, Lukasz, Hogan, James D., Sano, Tomoko, Shaeffer, Matthew
This study investigates the effects of the processing-induced defect population on the dynamic compressive strength and failure of a hot-pressed boron carbide. Quantitative microscopic analysis was used to determine the distributions of three types of processing-induced inhomogeneities: aluminum...
-
2017-04-01
Hogan, James D., Farbaniec, Lukasz, Mallick, Debjoy, Domnich, Vladislav, Kuwelkar, Kanak, Sano, Tomoko, McCauley, James W., Ramesh, Kaliat T.
In this paper, the impact-induced fragmentation of a commercially available hot-pressed boron carbide is explored. Fragmentation has been noted previously by many authors to be important in the impact performance of advanced ceramics, and so this paper seeks to provide some of the first...