Theses and Dissertations
This collection contains theses and dissertations of graduate students of the University of Alberta. The collection contains a very large number of theses electronically available that were granted from 1947 to 2009, 90% of theses granted from 2009-2014, and 100% of theses granted from April 2014 to the present (as long as the theses are not under temporary embargo by agreement with the Faculty of Graduate and Postdoctoral Studies). IMPORTANT NOTE: To conduct a comprehensive search of all UofA theses granted and in University of Alberta Libraries collections, search the library catalogue at www.library.ualberta.ca - you may search by Author, Title, Keyword, or search by Department.
To retrieve all theses and dissertations associated with a specific department from the library catalogue, choose 'Advanced' and keyword search "university of alberta dept of english" OR "university of alberta department of english" (for example). Past graduates who wish to have their thesis or dissertation added to this collection can contact us at erahelp@ualberta.ca.
Items in this Collection
-
Fall 2015
The present research has been done with the intent of evaluating the corrosion resistance and cracking susceptibility of some commercial candidate alloys that can be potentially used in Gen-IV supercritical water reactor (SCWR). The mechanism of the crack initiation in austenitic alloys exposed...
-
Spring 2013
As the Supercritical Water-cooled Reactor (SCWR) shows a promising future, the corrosion behavior of candidate materials has attracted great interest. In this study, experimental investigation was conducted to evaluate the corrosion behavior of the ferritic-martensitic steels designed for the use...
-
Effects of Oxide Additions on the Corrosion Behaviour of Cr2O3 Based Ceramics in High Temperature Supercritical Water Environment
DownloadFall 2012
This investigation is aimed at developing ceramic materials applied in supercritical water, which is being considered as coolant for one of the next generation nuclear reactors. Cr2O3, a primary protective film on stainless steels, was found to be unstable in SCW due to the formation of soluble...
-
Investigation of Corrosion and Crack Morphology Behavior under Disbonded Coatings on Pipelines
DownloadFall 2015
Coating disbondment on pipelines is a common phenomenon that leads to exposure of the pipeline metal to the surrounding soil and ground water solutions. The exposure of pipelines to those corrosive environments is associated with development of corrosion and Stress Corrosion Cracking (SCC) on the...
-
Investigation of Surface Crack Growth Behaviour Under Variable Pressure Fluctuations in Near-Neutral pH Environments
DownloadFall 2017
The goal of this investigation was to study the corrosion fatigue behaviour and mechanisms of surface cracks, semi-elliptical in shape, when exposed to near-neutral pH environments conducive to the environments experienced in the field. To better simulate field conditions, while avoiding the...