Design and processing conditions of hypoeutectic Al-Cu-Sc alloys for maximum benefit of scandium
Download2017-01-01
Bogno, A.-A., Henein, H., Gallerneault, M.
Addition of Sc to Al-Cu is reported to be responsible for a high precipitation hardening upon heat treatment and serves as a good grain refiner. However, Scandium is presently very expensive, therefore, getting maximum benefit from a minimum addition would be economically of value. This work...
-
EFFECTS OF SCANDIUM ON HYPO-EUTECTIC ALUMINUM COPPER MICROSTRUCTURES UNDER LOW SOLIDIFICATION RATE CONDITIONS
Download2017-11-01
Bogno, A.-A., Valloton, J., Henein, H., Ivey, D.G., Locock, A.J., Gallerneault, M.
This work addresses the microstructures and mechanical properties of Al-4.5 wt% Cu alloys containing 0.1, 0.2 and 0.4 wt% Sc that were solidified under low cooling rate conditions (< 1ºC/s) and then heat treated. The samples were solidified in a differential scanning calorimeter before being heat...
-
2019-01-01
Bogno, A.-A., Henein, H., Ivey, D.G., Valloton, J., Reinhart, G., Sediako, D., Gallerneault, M.
This paper reports on the characterization of rapidly solidified Al-4.5 wt% Cu-xSc (x= 0.1, 0.2 or 0.4 wt %). The effect of micro-additions of Sc (up to 0.4 wt %) was examined through microstructural analysis of rapidly solidified, as well as aged samples, by means of electron microscopy, x-ray...
-
2022-01-01
Henein, H., Bogno, A.-A., Yin, S., Natzke, P., Gallerneault, M.
Scandium (Sc) is an expensive alloying element which has an important effect on the properties of aluminum alloys. It is of interest to determine for a variety of solidification conditions the effect of minor addition, in the hypoeutectic levels, of Sc on Al alloys. This study builds on past work...
-
2021-01-01
Yin, S., Bogno, A.-A., Henein, H., Gallerneault, M.
This paper studies the solidification of hypoeutectic Al–Mg–Sc powders and spray deposited (SD) strips, generated by Impulse Atomization. The effects of Mg content in hypoeutectic Al–Mg–Sc was examined with respect to the extended solid solubility of Mg and Sc in α–Al, microstructure refinement...