Search
Skip to Search Results- 1Abtahi, Shaghayegh
- 1Aghaie, Ermia
- 1Ahmed, E.
- 1Ahmed, Ezz Q
- 1Arango Vasquez,Daniela
- 1Behnamian, Yashar
- 24Graduate and Postdoctoral Studies (GPS), Faculty of
- 24Graduate and Postdoctoral Studies (GPS), Faculty of/Theses and Dissertations
- 1Chemical and Materials Engineering, Department of
- 1Chemical and Materials Engineering, Department of/Research Articles and Materials (Chemical and Materials Engineering)
- 1Mechanical Engineering, Department of
- 1Mechanical Engineering, Department of/Progress in Canadian Mechanical Engineering, Volume 5
- 5Chen, Weixing (Chemical and Materials Engineering)
- 5Luo, Jingli (Chemical and Materials Engineering)
- 2Li, Dongyang (Chemical and Materials Engineering)
- 2Mitlin, David (Chemical and Materials Engineering)
- 2Thundat, Thomas (Chemical and Materials Engineering)
- 1Al-Hussein, Mohamed (Civil and Environmental Engineering)
-
Investigation of Corrosion and Crack Morphology Behavior under Disbonded Coatings on Pipelines
DownloadFall 2015
Coating disbondment on pipelines is a common phenomenon that leads to exposure of the pipeline metal to the surrounding soil and ground water solutions. The exposure of pipelines to those corrosive environments is associated with development of corrosion and Stress Corrosion Cracking (SCC) on the...
-
Investigation of Highly Corrosion Resistant and Electrically Conductive Coatings on Metal Bipolar Plates Used in Polymer Electrolyte Membrane Fuel Cell
DownloadSpring 2019
There are apparent technical and economic advantages to replace carbon-based bipolar plates using metal bipolar plates (MBP) for applications in polymer electrolyte membrane fuel cell (PEMFC). However, MBP suffers from corrosion in the acidic environment of PEMFC, and the subsequently formed...
-
Investigation of Surface Crack Growth Behaviour Under Variable Pressure Fluctuations in Near-Neutral pH Environments
DownloadFall 2017
The goal of this investigation was to study the corrosion fatigue behaviour and mechanisms of surface cracks, semi-elliptical in shape, when exposed to near-neutral pH environments conducive to the environments experienced in the field. To better simulate field conditions, while avoiding the...
-
Spring 2017
Magnesium remarkably deserves considerable interest from industry especially transportation sector because of its high strength to weight ratio. However, poor wear resistance and low corrosion resistance of magnesium are barriers to extend use of its alloys. Yttrium is one of rare-earth elements...
-
The Role of Sulfur Species in Establishing the Corrosion Reactions in Refinery Metallurgies
DownloadSpring 2016
This thesis is focused on the studying the role that model sulfur-containing molecules have in corrosion reactions on relevant metallurgies. This was done by using a design of experiments where a number of sulfur-based compounds were reacted with various metallurgies. The 8 model sulfur compounds...
-
The Study of the Corrosion Behavior of Gas Nitriding Treated L80 Steel in Simulated Environment for the Slotted Liners of SAGD
DownloadSpring 2016
The oil sand in Alberta province is mainly extracted by Steam Assisted Gravity Drainage (SAGD) technique which employs the slotted liners as the primary sand screening system. However, the slotted liners made of L80 carbon steel suffer from severe corrosion and erosion problems in the downhole...